MIG/MAG welding wire

Category:

Description

 

Name electrode

standards

Ø mm

Package (Kg)

Chemical analysis

Mechanical properties
po (AW/KS)

Current, polarity, welding posit.

MG 2
AWS/ASME SFA 5.18 ER 70 S – 6

0,60

Package of wire can be 15 and 5 kg

C

0,08

Yield strength(N/mm2)

460

 

EN 440 G 42 4MG3Si1

0,80

Si

0,80

Tensile strength Rm (N/mm2) 530
DIN 8559 SG 2 CY 42 43

1,00

Mn

1,45

Elongation A5 (%) 29

1,20

P

<0.025

Impact energy (ISO-V) (J)

20˚C:115 J

S

<0.025

Unalloyed wire electrode for GMA (MIG/MAG) welding of general structural steels, pipe steels, and cast steels using CO2 or mixed shielding gases, depending on thickness of hte base metal. Generally used in steel construction, shipbuilding, machine, tank, boiler production, automotive industry. Preheating is required, depending on the plate thickness and carbon equivalent of the base metal. A thin and homogeneous copper coating increases electrical conductivity and protects the wire from rusting.
MG 3
AWS/ASME SFA 5.18 ER 70 S – 6

0,80

Package of wire can be 15 and 5 kg

C

0,08

Yield strength (N/mm2)

470

 

EN 440 G 46 4MG4Si1

1,00

Si

0,90

Tensile strength Rm(N/mm2)

550

DIN 8559 SG 3 CY 46 43

1,20

Mn

1,70

Elongation A5 (%)

27

1,60

P

<0.025

Impact energy (ISO-V) (J)

20˚C:100 J

S

<0.025

Unalloyed wire electrode for GMA (MIG/MAG) welding of general structural steels, pipes and cast steels by using CO2 or mixed shielding gases can be used depending on thickness of the base metal. Generally used in steel construction, machine, tank, boiler production. Preheating is required, depending on the plate thickness and carbon equivalent of the base metal. A thin and homogeneous copper coating increases electrical conductivity and protects the wire from rusting.
FCW 11
AWS/ASMESFA5.20 E 71 T – 1

1,20

Pakovanja žice su 15 kilograma

C

0,05

Yield strength (N/mm2)

>460

EN 758 T 46 2 PC 1

1,60

Si

0,55

Tensile strength Rm (N/mm2)

550-650

DIN 8559 SGR1CY4643

Mn

1,20

Elongation A5 (%)

>22

Impact energy (ISO-V) (J)

20˚C:>80J
-20˚C:>50J J

Rutile type flux cored wire with fast-freezing slag. Especially designed for welding with CO2 (carbondioxide) gas, in shipbuilding and steel construction. Owing to its easily controllable weld pool, electrode is well suited for positional welding with higher currents, resulting in increased deposition rates. Particularly suited for welding in the horizontal-vertical position, e.g. in tank welding. Electrode of 1.2 mm in diameter is also suitable for vertical-down welding. Low spatter loss, easy slag removal, finely ripped pore-free welds blending into base metal without undercut.